This research synthesised zinc oxide (ZnO) structure by a hydrothermal method.ZnO samples were prepared using different molarities of zinc (Zn) precursor, ranging from 0.10 to 0.16 M. Structural and morphological properties were characterised by X-ray diffraction (XRD) and scanning electron microscopy (SEM).The SEM images show that the ZnO samples are randomly oriented with average diameters of 209, 325, 295 and 348 nm when using 0.10, 0.12, 0.14 and 0.16 M of the precursor, respectively.The XRD patterns show that all samples are prominently grown along the three diffraction peaks at (001), (002) and (101) planes.The average crystallite sizes for the ZnO structure with 0.10, 0.12, 0.14 and 0.16 M precursor are 48, 51, 49 and 31 nm, respectively.
This research synthesised zinc oxide (ZnO) structure by a hydrothermal method. ZnO
samples were prepared using different molarities of zinc (Zn) precursor, ranging from 0.10 to 0.16 M.
Structural and morphological properties were characterised by X-ray diffraction (XRD) and scanning
electron microscopy (SEM). The XRD patterns show that all samples are prominently grown along the
three diffraction peaks at (001), (002) and (101) planes. The ZnO sample with 0.16 M Zn precursor has
the highest peak orientation along the (002) plane. The average crystallite sizes for the ZnO structure
with 0.10, 0.12, 0.14 and 0.16 M precursor are 48, 51, 49 and 31 nm, respectively. ZnO sample prepared
at 0.16 M has the smallest crystallite size and the lowest tensile strain. The SEM images show that
the ZnO samples are randomly oriented with average diameters of 209, 325, 295 and 348 nm when
using 0.10, 0.12, 0.14 and 0.16 M of the precursor, respectively. The electrochemical behaviour of the
ZnO structure was determined through cyclic voltammetry (CV) measurement. In the CV curve,
the calculated specific capacitance for the ZnO sample prepared at 0.16 M has the highest value of
3.87 Fg−1. The ZnO sample prepared at 0.10 M has the lowest specific capacitance value of 2.11 Fg−1.
Therefore, changing the molarity of the Zn precursor could change the structural and electrochemical
properties. ZnO sample prepared with 0.16 M of the precursor provides the optimal result
Summarize English and Arabic text using the statistical algorithm and sorting sentences based on its importance
You can download the summary result with one of any available formats such as PDF,DOCX and TXT
ٌYou can share the summary link easily, we keep the summary on the website for future reference,except for private summaries.
We are working on adding new features to make summarization more easy and accurate
أنه انفصل عن عصره، فقد مضى يزاوج بين الماضي والحاضر، يتلقى الماضي وبحباه، ويتلقى الحاضر ويحياه. الم...
تم حساب المتوسط الحسابي والانحراف المعياري للدرجة الكلية للبُعد الأول من أداة الدراسة، والمتعلق بتفع...
الأسس التي تقوم عليها الطريقة: جاءت الطرائق المثلى نتيجة اختبار طويل وتجريب علمي وملاحظات كثيرة وتأم...
ﺔ ﺗُﻌﺪ اﻷﺳﺮة أﺳﺎس اﻟﻤﺠﺘﻤﻊ، وھﻲ اﻟﻤﺆﺳﺴﺔ اﻟﺘﻲ ﺗﻘﻮم ﻋﻠﻰ اﻟﻤﻮدة واﻟﺮﺣﻤﺔ واﻟﺘﻌﺎون ﺑﯿﻦ اﻟﺰوﺟﯿﻦ، وﻟﺬﻟﻚ أوﻟﺖ...
دورالقيادة الإدارية في تحسين الأداء الوظيفي: يجب على المنشأة أو الوزارة أو الهيئة أو أي كان مسماها ...
- نظرًا لأهمية أصول الفقه في فهم الأدلة، فإن النقطة المركزية في كثير من الاتجاهات الفكرية الحديثة هي...
مراجعة نقدية لدراسة: أثر العلاج المعرفي السلوكي المركز على الصدمة والعلاج بالموسيقى في خفض أعراض قلق...
لا يقتصر تأثير الذكاء الاصطناعي على الجوانب التقنية فقط، بل يمتد أيضًا إلى الجوانب الأخلاقية والمهني...
قوله: (في ظاهره) متعلق بيضطر: أي في الأفعال المتعلقة بظاهره كالصلاة. قوله: (وباطنه) أي والأفعال المت...
الإعداد العميق والتعليم الروحي الفعال مقدمة فخ المظاهر الخارجية يبدأ النقاش بتشبيه بليغ لمطعم فاخر ي...
شهدت جبهة الضالع خلال الساعات الماضية تطورات ميدانية متسارعة، بعد أن تمكنت القوات المسلحة الجنوبية م...
كشف مصدر حقوقي في العاصمة المؤقتة عدن، عن غموض يكتنف تحركات وبرنامج عمل لجنة العقوبات الدولية المتوا...